• Medical device class IIa
• 35% Translucency
Flexural strength: > 1200 MPa
E-Modulus: > 200 GPa
• WAK 25 – 500 °C: 10*10⁻⁶
• Recommended sintering temperature: 1,450 – max. 1,530 degrees

• Reduced crowns and bridges in the front and
Molar area
• Large-span bridges up to 16 sections
Telescope Primary Parts
• Implant-supported (directly screwed) bars and bridges

Excellent translucency, ideal for masking
• Increased strength and excellent
Bending strength for up to 16-link structures
• With standard dip and brush paints
to dye well
Works with all standard
Veneers