Zirconia
Highly translucent
MultiColor
Highly translucent zirconia with very good flexural strength, also suitable for large circular bridges. This highly translucent zirconium oxide is provided with up to 8 colour layers - in a flowing transition without visible steps. This way, the natural colour gradient of a tooth from cervical, dentin to incisal is reproduced absolutely realistically.
The highly aesthetic result can often be used in the posterior region without further finishing. Perfectionists will add a few more brush strokes and the aesthetic result is comparable to a veneered work!
Further information
- Technical data
- Indications
- Features
- Downloads
- Medical device class IIa
- 41% translucency
- Flexural strength: > 1100 MPa
- Modulus of elasticity: > 200 GPa
- CTE 20 - 500 °C: 10*10-6
- Released sintering temperature: 1,450 - max. 1,530 degrees
- Crowns and large-span bridges up to 14 units
- Fully anatomical crowns and bridges
- Reduced crowns and bridges, e.g. for minimal layering
in the anterior region
- Telescopic primaries
- Implant-supported (directly screw-retained) bars and bridges
- High translucency for highly aesthetic fully anatomical
crowns and bridges
- High strength for up to 14-unit restorations, i.e. even
large posterior restorations or circular restorations are possible
completely monolithic with very high aesthetics
- The up to 8 shade layers reproduce the natural
structure of a tooth - in a flowing shade gradient
without steps
- The shade gradient completely penetrates the zirconia. Even
after grinding, there are no white spots
- Works with all commercially available veneering ceramics